Effect of Mold Temperature and Pouring Temperature on the Crack Behavior of Composite Water-Soluble Salt Cores
Jingkai Zhang, Yang Li, Lai Song, Weihua Liu & Xue Zou Abstract This study analyzes the effects of different pouring temperatures and mold temperatures on ...
![Figure 8(a) Inverse pole figure maps for halite grains with large Kristallbrocken grains labelled 1–5. (b) Pole figures of fine-grained matrix halite excluding five Kristallbrocken grains show no significant crystallographic preferred orientation (CPO). (c) Kernel average misorientation (KAM) map overlaid with white low- and high-angle grain boundaries (misorientation >5∘). KAM map was calculated over a distance of 40 µm (second neighbour) with a threshold of 3∘ in order to enhance the small-angle subgrain boundaries. KAM shows subgrain-free matrix halite with few exceptions in large matrix halite grains, Kristallbrocken 1 and 5 with subgrains, and subgrains in boudin necks of Kristallbrocken 3 and 4. (d) Cumulative reference orientation deviation map over the areas of Kristallbrocken 3 and 4, based on more highly resolved EBSD measurements. Reference points for each of the two grains are indicated. Panels (a) and (b) consist of 30 individual measurements, which due to image distortion under 70∘ tilt cannot be stitched perfectly. Therefore, in some cases an artificial separation of areas belonging to the same grain is visible](https://castman.co.kr/wp-content/uploads/Figure-8a-Inverse-pole-figure-maps-for-halite-grains-with-large-Kristallbrocken-grains-labelled-1–5-287x300.png)
Large grain-size-dependent rheology contrasts of halite at low differential stress: evidence from microstructural study of naturally deformed gneissic Zechstein 2 rock salt (Kristallbrockensalz) from the northern Netherlands
Jessica Barabasch,Joyce Schmatz,Jop Klaver,Alexander Schwedt,and Janos L. Urai Abstract Constitutive laws to predict long-term deformation of solution-mined caverns and radioactive-waste ...
![High-Temperature Mechanical Properties of NaCl–Na2CO3 Salt-Mixture Removable Cores for Aluminum Die-Casting](https://castman.co.kr/wp-content/uploads/High-Temperature-Mechanical-Properties-of-NaCl–Na2CO3-Salt-Mixture-Removable-Cores-for-Aluminum-Die-Casting-239x300.png)
High-Temperature Mechanical Properties of NaCl–Na2CO3 Salt-Mixture Removable Cores for Aluminum Die-Casting
Katsunari Oikawa, Kazuhiro Sakakibara, Youji Yamada, Koichi Anzai Abstract The NaCl–Na2CO3 salt mixture is proposed as a water-soluble core material for aluminum die-casting processes ...
![Fabrication and Characterization of High-strength Water-soluble Composite Salt Cores via Layered Extrusion Forming](https://castman.co.kr/wp-content/uploads/Fabrication-and-Characterization-of-High-strength-Water-soluble-Composite-Salt-Cores-via-Layered-Extrusion-Forming-300x177.png)
Fabrication and Characterization of High-strength Water-soluble Composite Salt Cores via Layered Extrusion Forming
Zheng Chen, Suo Fan, Lei Peng, Yincheng Wang, Xiaolong Gong, Xinwang Liu & Zitian Fan International Journal of Metalcasting (2022)Cite ...
![Fabrication of high-strength salt cores for manufacturing hollow aluminum alloy die castings](https://castman.co.kr/wp-content/uploads/Fabrication-of-high-strength-salt-cores-for-manufacturing-hollow-aluminum-alloy-die-castings-300x192.png)
Fabrication of high-strength salt cores for manufacturing hollow aluminum alloy die castings
Xiaolong Gong, Xiongjie Xiao, Xinwang Liu & Zitian Fan Received 03 Apr 2022, Accepted 21 Apr 2022, Published online: 13 May ...
![Fig. 12. Stress condition on salt core surface immediately after the first impact of the semi solid melt. The flow velocity before impact is 4.55 m/s. The maximum stress on the lower core side is approximately 2.3 MPa.](https://castman.co.kr/wp-content/uploads/s.-The-maximum-stress-on-the-lower-core-side-is-approximately-2.3-MPa.-300x169.png)
About the impact on gravity cast salt cores in high pressure die casting and rheocasting
Author links open overlay panelAndreasSchillingDanielSchmidtJakobGlückNiklasSchwenkeHusamSharabiMartinFehlbierShow moreAdd to MendeleyShareCite https://doi.org/10.1016/j.simpat.2022.102585Get rights and content Under a Creative Commons license Open access Abstract ...
![First-Principles Calculation and Mechanical Properties of NaCl–Na2SO4 Composite Water-Soluble Salt Core](https://castman.co.kr/wp-content/uploads/First-Principles-Calculation-and-Mechanical-Properties-of-NaCl–Na2SO4-Composite-Water-Soluble-Salt-Core-300x173.png)
First-Principles Calculation and Mechanical Properties of NaCl–Na2SO4 Composite Water-Soluble Salt Core
Xue-ting Wang, Wei-hua Liu, Xuan-yu Liu & Lai Song International Journal of Metalcasting (2022)Cite this article 84 Accesses1 CitationsMetricsdetails Abstract ...
![Figure 10.2. Salt core produced in high temperature and long time](https://castman.co.kr/wp-content/uploads/image-29-300x249.png)
Development of Salt Core Use as an Alternative in Aluminum Alloy Castings.
Tülay Hançerlioğlu 1*1 R&D Department Nemak İzmir Döküm San.A.Ş. tulay.hancerlioglu@nemak.comOrcid: 0000-0003-2373-4405Received: 6 December 2021Accepted: 1 June 2022DOI: 10.18466/cbayarfbe.1033177 Abstract For ...
![Figure 4. Water-soluble experiments of the KNO3-based salt core strengthened by 30 wt.% glass fiber (size = 25 lm) in 80 C water: (a) 0 min; (b) 6 min; (c) 12 min; (d) 18 min](https://castman.co.kr/wp-content/uploads/image-13-300x77.png)
Effects of glass fiber size and content on microstructures and properties of KNO3-based water-soluble salt core for high pressure die casting
Xiaolong Gong, Wenming Jiang , Fuchu Liu, Zhiyuan Yang, Feng Guan, and Zitian FanState Key Laboratory of Materials Processing and ...
![In-Mold Coating in Pressing of Natural-Fiber-Reinforced Salt Cores for High-Pressure Die-Casting Applications](https://castman.co.kr/wp-content/uploads/In-Mold-Coating-in-Pressing-of-Natural-Fiber-Reinforced-Salt-Cores-for-High-Pressure-Die-Casting-Applications-300x138.png)
In-Mold Coating in Pressing of Natural-Fiber-Reinforced Salt Cores for High-Pressure Die-Casting Applications
Patricia Erhard, Dominik Boos & Daniel Günther Proceedings of the Munich Symposium on Lightweight Design 2021 pp 35–43Cite as In-Mold ...