Fig. 6—Development of solution-treatment schedule for alloy 380

Published at 662 × 391 in Heat Treatment of High-Pressure Die Castings

Fig. 6—Development of solution-treatment schedule for alloy 380. Each sample was immersed at temperature for a total of 15 min. Metal velocity at the gate was 26 m/s.