Fig. 8. Cold flakes observed in the HPDC castings having step thickness of (a) 2 mm, and (b) 10 mm. The red dashed line in each image indicates the flat edge of the cold flake particle. (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Published at 1092 × 390 in Evaluation of detrimental effect on the ductility caused by the inhomogeneous skin and casting defects in a high pressure die cast recycled secondary alloy

Fig. 8. Cold flakes observed in the HPDC castings having step thickness of (a) 2 mm, and (b) 10 mm. The red dashed line in each image indicates the flat edge of the cold flake particle. (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Fig. 8. Cold flakes observed in the HPDC castings having step thickness of (a) 2 mm, and (b) 10 mm. The red dashed line in each image indicates the flat edge of the cold flake particle. (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Fig. 8. Cold flakes observed in the HPDC castings having step thickness of (a) 2 mm, and (b) 10 mm. The red dashed line in each image indicates the flat edge of the cold flake particle. (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)