Fig. 5. Localized plastic strains generated by the pore

Published at 777 × 560 in Conditions for blister formation during thermal cycles of Al–Si–Cu–Fe alloys for high pressure die-casting

Fig. 5. Localized plastic strains generated by the pore with C/A = 0.06, pore volume of 7.5°10−6 mm3 , H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures during heating: a) 25 °C; b) 360 °C; c) 390 °C; d) and at room temperature (T0 = 25 °C) after cooling. Also in these figures the plastic strains are plotted on the deformed shape and the notes about the color scales for Fig. 4 are to be considered.

Fig. 5. Localized plastic strains generated by the pore with C/A = 0.06, pore volume of 7.5°10−6 mm3
, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures
during heating: a) 25 °C; b) 360 °C; c) 390 °C; d) and at room temperature (T0 = 25 °C) after cooling. Also in these figures the plastic strains are plotted on the deformed shape and the
notes about the color scales for Fig. 4 are to be considered.

Fig. 5. Localized plastic strains generated by the pore with C/A = 0.06, pore volume of 7.5°10−6 mm3
, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures
during heating: a) 25 °C; b) 360 °C; c) 390 °C; d) and at room temperature (T0 = 25 °C) after cooling. Also in these figures the plastic strains are plotted on the deformed shape and the
notes about the color scales for Fig. 4 are to be considered.