Fig. 4. Localized plastic strains generated by the pore with C/A = 0.53, 7.5°10−6 mm3 pore volume, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures during heating: a) 25 °C; b) 420 °C; c) 440 °C and d) at room temperature T0 = 25 °C after cooling. Note that the color scale for plastic strains, plotted on the deformed shape limited by the value of maximum principal plastic strains equal to 0.2 mm/mm.

Published at 769 × 554 in Conditions for blister formation during thermal cycles of Al–Si–Cu–Fe alloys for high pressure die-casting

Fig. 4. Localized plastic strains generated by the pore with C/A = 0.53, 7.5°10−6 mm3 pore volume, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures during heating: a) 25 °C; b) 420 °C; c) 440 °C and d) at room temperature T0 = 25 °C after cooling. Note that the color scale for plastic strains, plotted on the deformed shape limited by the value of maximum principal plastic strains equal to 0.2 mm/mm.

Fig. 4. Localized plastic strains generated by the pore with C/A = 0.53, 7.5°10−6 mm3 pore volume, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures
during heating: a) 25 °C; b) 420 °C; c) 440 °C and d) at room temperature T0 = 25 °C after cooling. Note that the color scale for plastic strains, plotted on the deformed shape limited by the
value of maximum principal plastic strains equal to 0.2 mm/mm.

Fig. 4. Localized plastic strains generated by the pore with C/A = 0.53, 7.5°10−6 mm3 pore volume, H = 0.0245 mm and reference inner pressure ps of 30 MPa at different temperatures
during heating: a) 25 °C; b) 420 °C; c) 440 °C and d) at room temperature T0 = 25 °C after cooling. Note that the color scale for plastic strains, plotted on the deformed shape limited by the
value of maximum principal plastic strains equal to 0.2 mm/mm.