Fig. 6. BSE-images of the areas the EPMA-mappings where conducted (a) 1 mm samples cast from alloy 226D without Sr addition and (b) 1 mm samples cast from alloy 226D with 0.034 wt.-% Sr.

Published at 1568 × 468 in Increasing the conductivity of aluminium high-pressure die casting alloy AlSi9Cu3Fe (226D) by Sr modification of eutectic and intermetallic phases