Figure 2.3: Phases precipitated out during solidification as a function of iron content and cooling rate [47]. The Al-Fe-Si ternary eutectic composition occurs at about 0.8% Fe.

Published at 1139 × 781 in High Temperature Strength Reduces Soldering In Aluminum High Pressure Die Casting

Figure 2.3: Phases precipitated out during solidification as a function of iron content and cooling rate [47]. The Al-Fe-Si ternary eutectic composition occurs at about 0.8% Fe.

Figure 2.3: Phases precipitated out during solidification as a function of iron content and
cooling rate [47]. The Al-Fe-Si ternary eutectic composition occurs at about 0.8% Fe.