Fig. 7. OM images showing the casting defects produced in the as-cast AlSi10MnMg(Fe) alloy: (a) Cold flake with conspicuous flat edge indicated by red arrows, and (b) Cold shot. (Adapted with permission from Dalai et al. [19]). (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Published 04/09/2025 at 1094 × 394 in Evaluation of detrimental effect on the ductility caused by the inhomogeneous skin and casting defects in a high pressure die cast recycled secondary alloy

Fig. 7. OM images showing the casting defects produced in the as-cast AlSi10MnMg(Fe) alloy: (a) Cold flake with conspicuous flat edge indicated by red arrows, and (b) Cold shot. (Adapted with permission from Dalai et al. [19]). (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Fig. 7. OM images showing the casting defects produced in the as-cast AlSi10MnMg(Fe) alloy: (a) Cold flake with conspicuous flat edge indicated by red arrows, and (b) Cold shot. (Adapted with permission from Dalai et al. [19]). (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)

Fig. 7. OM images showing the casting defects produced in the as-cast AlSi10MnMg(Fe) alloy: (a) Cold flake with conspicuous flat edge indicated by red arrows, and (b) Cold shot. (Adapted with permission from Dalai et al. [19]). (For interpretation of the references to color in this figure legend, the reader is referred to the web version of this article.)