Figure 6.1 Optical microscope image of the reference sample (a) and the one sandblasted under 5 bar for 1 minute (b); magnification is equal to 180. A change in surface topology can be observed due to increased roughness caused by sandblasting.

Published at 801 × 390 in Properties of the nanocrystalline layers obtained by methods of severe plastic deformation in metals and alloys for biomedical applications

Figure 6.1 Optical microscope image of the reference sample (a) and the one sandblasted under 5 bar for 1 minute (b); magnification is equal to 180. A change in surface topology can be observed due to increased roughness caused by sandblasting.

Figure 6.1 Optical microscope image of the reference sample (a) and the one sandblasted under 5 bar for 1 minute (b); magnification is equal to 180. A change in surface topology can be observed due to increased roughness caused by sandblasting.

Figure 6.1 Optical microscope image of the reference sample (a) and the one sandblasted under 5 bar for 1 minute (b); magnification is equal to 180. A change in surface topology can be observed due to increased roughness caused by sandblasting.