Figure 9. Cross-sectional area of UL-sample etched with two percent aqueous sodium hydroxide solution and alkaline potassium permanganate solution according to Weck et al. [22]. […] A coarser dendrite structure can be seen in the area above the salt support structure.

Published at 1143 × 800 in Influence of Salt Support Structures on Material Jetted Aluminum Parts

Figure 9. Cross-sectional area of UL-sample etched with two percent aqueous sodium hydroxide solution and alkaline potassium permanganate solution according to Weck et al. [22]. [...] A coarser dendrite structure can be seen in the area above the salt support structure.

Figure 9. Cross-sectional area of UL-sample etched with two percent aqueous sodium hydroxide solution and alkaline potassium permanganate solution according to Weck et al. [22]. […] A coarser dendrite structure can be seen in the area above the salt support structure.

Figure 9. Cross-sectional area of UL-sample etched with two percent aqueous sodium hydroxide solution and alkaline potassium permanganate solution according to Weck et al. [22]. [...] A coarser dendrite structure can be seen in the area above the salt support structure.